Zeroflame AquaSteel WB+ intumescent coating provides an easy and efficient fire protection alternative to cladding structural steel members in fire rated board! Zeroflame have combined the ability to protect standard steel sizes and profiles for both 30 and 60 minutes fire resistance in a single product. 

Please Note this has a 2-3 working day delivery lead time.

Availability: 9 In Stock
Sku: A000

Zeroflame continue to make things simpler

Zeroflame AquaSteel WB+ intumescent coating provides an easy and efficient fire protection alternative to cladding structural steel members in fire rated board! Zeroflame have combined the ability to protect standard steel sizes and profiles for both 30 and 60 minutes fire resistance in a single product. 

By creating AquaSteel WB+ they have fast tracked the time consuming process of gathering all details on the steel members and calculating the exact of amount of materials needed for each steel member. This makes things so much easier!

Zeroflame have also produced a topcoat for AquaSteel WB+, you can find their topcoat here.

 

  • Final Finish - Natural.
  • Zeroflame Fire Retardant Treatment achieves Class 1 only, on veneer and plywood laminates, due to the bonding glues resisting penetration. 
  • Discolouration may occur on some types of timber or on heavily knotted wood. If this is a concern it is recommended that a sample area is completed before application to the whole project. Alternatively, application of a compatible varnish or stain may help overcome this phenomenon if it is unacceptable.
  • Zeroflame Fire Retardant Treatment is not suitable for wood-derived particle board or similar as it cannot penetrate. Zeroflame Fire Retardant Paint is recommended instead.

Certification

Each tin has a certificate application form on the back of the label. To receive a 'Certificate of Supply' for your purchase, after application of the product, simply complete the form on the label and send to the stated address and a certificate will be returned to you within 7-10 working days.

Preparation

Stir Zeroflame Fire Retardant Paint thoroughly until free of lumps. Substrates must be dry (moisture content must not exceed 15%), free from dust, wax, grease, dirt, resin, etc. Existing coatings with poor adhesion must be completely removed. Coatings containing lime, chalk or lithopone should be removed.

Application

Airless Spray

  • Zeroflame Fire Retardant Paint should be applied undiluted
  • Airless spray equipment with pressure ratio 30:1
  • Hose diameter not below 3/8"
  • Whipline 1.5-2m. NW6 may be used
  • Recommended tip size 0.34-0.66mm or 0.17-0.027"
  • Hoses must be used only for water based coatings

Brush/Roller

  • Zeroflame Fire Retardant Paint should be applied in supplied viscosity

Conditions

Object temperature not below +10°C, to max. +40°C, relative humidity max. 70%.

Application temperature shall be at least ≥ 3°C above dew point. In case relative humidity exceeds 80%, special measures must be taken to prevent condensation forming when applying. If the moisture content of the substrate exceeds 15%, the coating is unlikely to dry and blooming may occur. Moisture content should be at, or near that anticipated when in use.

Drying

At approx. 20°C temperature and 65% relative humidity approx. 6 hours. Lower temperatures and higher relative humidity may extend drying times. Allow 48 hours before overcoating.

Cleaning

Immediately after use, clean the equipment with water.

Zeroflame AquaSteel WB+ intumescent coating provides an easy and efficient fire protection alternative to cladding structural steel members in fire rated board! Zeroflame have combined the ability to protect standard steel sizes and profiles for both 30 and 60 minutes fire resistance in a single product. 